典型聚酯涂层镀锌钢板的受热痕迹特征研究

doi:10.16265/j.cnki.issn1003-3033.2020.01.010

中国安全科学学报 ›› 2020, Vol. 30 ›› Issue (1): 61-65.doi: 10.16265/j.cnki.issn1003-3033.2020.01.010

典型聚酯涂层镀锌钢板的受热痕迹特征研究

金静¹ 讲师, 姚子嘉¹, 刘玲¹ 副教授, 张金专¹ 教授, 周广英² 高级工程师, 王平³ 工程师

1.中国人民警察大学防火工程学院,河北廊坊 065000;
2.黑龙江大庆消防救援支队,黑龙江大庆163000;
3.河北廊坊消防救援支队,河北廊坊 065000

收稿日期:2019-10-10 修回日期:2019-12-21 出版日期:2020-01-28 发布日期:2021-01-22
作者简介:金静 (1986—),女,安徽宿州人,博士,讲师,主要从事与火灾调查相关的研究 E-mail:jinj@iccas.ac.cn
基金资助:
“十三五”国家科技基础性工作专项(SQ2015FY3120051);河北省重点研发计划(18215416)。

Heated trace features of galvanized steel plate coated with polyester

JIN Jing¹, YAO Zijia¹, LIU Ling¹, ZHANG Jinzhuan¹, ZHOU Guangying², WANG Ping³

1. School of Fire Protection Engineering, Chinese People's Police University, Langfang Hebei 065000, China;
2. Daqing Fire Rescue Brigade, Daqing Heilongjiang 163000, China;
3. Langfang Fire Rescue Brigade, Langfang Hebei 065000, China

Received:2019-10-10 Revised:2019-12-21 Online:2020-01-28 Published:2021-01-22

摘要/Abstract

摘要： 为研究聚酯涂层镀锌钢板高温受热后的痕迹特征变化,选择热塑性丙烯酸涂覆的镀锌钢板为研究对象,在对其涂层进行热重分析的基础上,讨论钢板在不同受热温度及时间作用下的痕迹特征。结果表明:温度升高至360 ℃时,热塑性丙烯酸涂层发生明显的热解炭化,带涂层钢板的质量降低;在410～590 ℃温度范围内,涂层开裂、脱落,聚酯涂层钢板整体质量进一步降低;受热温度继续升高至600 ℃,镀锌层露出并发生氧化破坏后,钢板基体露出并发生氧化,钢板质量回升,局部区域不同程度的氧化过程导致整块钢板呈现出多层次且不均匀的受热痕迹;受热时间对痕迹的影响在高温下更为显著。

关键词: 镀锌钢板, 聚酯涂层, 热失重分析, 受热痕迹, 高温氧化

Abstract: In order to study heated trace features of polyester coated galvanized steel sheet, thermoplastic acrylic coated galvanized steel sheet was selected as research object, and features of its heated trace under different temperature and duration was discussed based on thermogravimetric analysis of its coating. The results show that the coating obviously undergoes pyrolysis carbonization when temperature rises to 360 ℃, resulting in mass loss of steel. With cracking and shedding of the coating at temperature between 410 ℃ and 590 ℃, steel mass further decreases. As galvanized layer exposes and oxidizes at 600 ℃, steel plate is exposed and oxidized, resulting in recovery of mass, and multi-layer and non-uniform heating traces are presented for the whole plate caused by oxidization of its parts at different degree. Comparatively, influence of heating duration on traces is more significant at higher temperature.

Key words: galvanized steel sheet, polyester coating, thermogravimetric analysis, heated traces, high-temperature oxidation

中图分类号:

X928. 7

金静, 姚子嘉, 刘玲, 张金专, 周广英, 王平. 典型聚酯涂层镀锌钢板的受热痕迹特征研究[J]. 中国安全科学学报, 2020, 30(1): 61-65.

JIN Jing, YAO Zijia, LIU Ling, ZHANG Jinzhuan, ZHOU Guangying, WANG Ping. Heated trace features of galvanized steel plate coated with polyester[J]. China Safety Science Journal, 2020, 30(1): 61-65.

参考文献

[1] NFPA 921-2017,Guide for fire and explosion investigations[S].
[2] CHEN R Y, YEUN W Y D. Review of the high-temperature oxidation of iron and carbon steels in air or oxygen[J]. Oxidation of Metals, 2003, 59(5): 433-468.
[3] BERTRAND N, DESGRANDES C, POQUILLON D. Iron oxidation at low temperature(260-500 ℃) in air and the effect of water vapor[J]. Oxidation of Metals, 2010, 73(1): 139-162.
[4] GLEESON B, YOUNG D J. High temperature corrosion and oxidation of metals[J]. Oxidation of Metals, 2011, 75(3/4): 121-123.
[5] BONIARDI M, CASAROLI A. Influence of heat on non-ferrous objects: metallurgical analysis in fire scene investigations[J]. Fire Technology, 2014, 50(6): 1 335-1 356.
[6] BONIARDI M, CASAROLI A. In-depth approach to fire investigations: microstructural analysis of metallic materials[J]. Fire and Materials, 2015, 39: 600-618.
[7] XIE Dongbai, SHAN Guo, SHI Deng, et al. Investigations on oxidation and microstructure evolution of pure Cu in simulated air-kerosene combustion atmospheres[J]. Fire and Materials, 2016, 41(6): 614-624.
[8] XIE Dongbai, SHAN Guo, LU Shilei. Oxidation behavior of carbon steel in simulated kerosene combustion atmosphere: a valuable tool for fire investigations[J]. Fire and Materials, 2017, 42(2): 156-163.
[9] 孙强, 陆守香. 火灾环境下具有弹性支座钢构件的稳定性能[J]. 中国安全科学学报, 2004, 14(2): 20-23.
SUN Qiang, LU Shouxiang. Stabilizing performance of steel members with elastic support under fire condition[J]. China Safety Science Journal, 2004, 14(2): 20-23.
[10] 牛会永, 周心权, 贾雨成. 基于金相分析技术的煤矿火灾事故调查试验研究[J]. 中国安全科学学报, 2010, 20(8): 71-75.
NIU Huiyong, ZHOU Xinquan, JIA Yucheng. Experimental research of fire accident investigation in coalmine based on metallographic analysis technique[J]. China Safety Science Journal, 2010, 20(8): 71-75.
[11] 陈克, 刘振刚, 邓松华, 等. 汽车车身燃烧残留痕迹特征的研究[J]. 消防科学与技术, 2007, 26(1): 101-103.
CHEN Ke, LIU Zhengang, DENG Songhua, et al. Study on characterist ics of burn patterns of vehicle body[J]. Fire Science and Technology, 2007, 26(1): 101-103.
[12] 鄂大志, 毛克明, 张明. 火灾现场金属变色痕迹识别智能方法[J]. 消防科学与技术, 2016, 35(12): 1 769-1 772.
E Dazhi, MAO Keming, ZHANG Ming. Intelligent identification method for mental color trace in fire scene[J]. Fire Science and Technology, 2016, 35(12): 1 769-1 772.
[13] 张雪宁, 邓亮, 张宇澍. 镀锌钢板受热氧化痕迹试验研究[J]. 消防科学与技术, 2017, 36(6): 880-885.
ZHANG Xuening, DENG Liang, ZHANG Yushu. Experiment study on thermal oxidation trace of galvanized steel sheet[J]. Fire Science and Technology, 2017, 36(6): 880-885.

典型聚酯涂层镀锌钢板的受热痕迹特征研究

Heated trace features of galvanized steel plate coated with polyester

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价